pressing temperature meaning in English
压制温度
Examples
- Effect of hot - pressing temperature and natural curing time on properties of fast - curing cement particle board
热压温度和养护时间对快速固化水泥刨花板性能的影响 - Under the same conditions of hot - pressing time , composite density , pe ratio , and resin content , the optimum properties of the composites can be obtained when hot - pressing temperature is 190 degrees c
当在热压时间、聚乙烯比例、施胶量、复合材料密度相同的条件下，热压温度为190时压制出的麦秸聚乙烯复合板材各项物理力学性能较好。 - An experiment was conducted to study the effects of hot - pressing temperature on properties of wheat straw - plastic composites made from wheat straw and recycled polyethylene ( pe ) using isocyanate as adhesive through multi - factor orthogonal experiment and single - factor experiment
摘要通过正交试验和单因子试验，以麦秸和废旧聚乙烯塑料为原料，使用异氰酸酯胶黏剂压制麦秸塑料刨花板，分析热压温度对麦秸聚乙烯复合材料性能的影响。 - The experimental results demonstrate that the suitable mea hot - pressing temperature and pressure are 120 and 15 . 5mpa , respectively . the optimum catalyst loading in anode is 4 mg pt / cm2 , and the best contents of nafion ionomer in anode and cathode layer are 45wt % and 35 . 3wt % , respectively
实验结果显示，制备膜电极时最佳的热压温度和压力分别为120和15 . 5mpa ；阳极催化剂的适宜载量为4mgpt / cm2 ；阳极和阴极催化剂层的nafion最优含量分别为45 . 0wt %和35 . 3wt % 。 - On the same condition of hot - pressing time , hot - pressing temperature and density of composite , the optimum properties of composite were obtained when recycled polypropylene content is 40 % by using mdi as coupling agent and recycled polypropylene content is 50 % by using ma as coupling agent
在热压时间、热压温度、复合材料密度相同的条件下，用异氰酸酯（简称mdi ）作偶联剂，聚丙烯用量40 %时复合材料的性能最佳；而用马来酸酐（简称ma ）作偶联剂，聚丙烯用量50 %时复合材料的性能最佳。